CORROLESS CCI 400
CORROSION INHIBITOR (WAX COATING)
DESCRIPTION
A blend of waxes and vapour
phase corrosion inhibitor (VCI), developed for outdoor
use under aggressive conditions. This product is also available in aerosol
cans as CCI 400A, when volume solids, drying times etc. may vary from
values given in the data sheet.
PRODUCTS :
Works by both contact and vapour phase inhibition
FEATURES AND : Suitable for application onto damp surfaces
RECOMMENDED :
Gives up to 4 years protection depending on environment
USES : Easily removed
and recoated
:
Applications include equipment, void spaces, structural steel, winches,
wire ropes, cranes, box sections etc.
TECHNICAL DATA
Volume Solids (+2%) : 55 %
Specific gravity : 0.9kg/litre
Film thickness : Wet Film
182 Microns. Dry Film 100 Microns
Mixing Ratio : Single pack
Theoretical Coverage : 5.5m²/litre. Practical coverage
rate can vary depending on application method, temperature, profile and porosity of
the substrate.
Pot Life (at 18⁰C) : Not Applicable
Drying Time (at 18⁰C) : Dries to a wax finish in 24 hours.
(at recommended dft)
Thinners and
Cleaning Solvent : Corroless Thinners No 2. (Solvent Gun Wash may be
used for cleaning only)
Finish :
Dull wax
Colours : Semi-translucent
light brown
Storage : Store in dry,
cool conditions and protect from frost.
CORROLESS CCI 400
CORROSION INHIBITOR (WAX COATING)
APPLICATION DETAILS
Recommended substrate Steel and most metallic substrates
Surface Preparation
No special surface preparation
is required, but the cleaner the substrate,
the more effective will be protection achieved from the product.
For the best results degrease using a water soluble degreaser
and prepare heavily corroded steel surfaces using rust scrapers,
wire brushes, needle guns, etc. to St2 standard of EN ISO 8501-1:
1988 or equivalent. wash down with fresh water and allow to
dry prior to application.
For
clean surfaces (e.g. production components, machinery casings etc)
degrease using a water soluble degreaser to remove dirt and oil/grease
deposits and allow to dry prior to application.
Application
|
Method
|
Airless
Spray
|
Conventional
Spray
|
Brush
|
Roller
|
|
Output Fluid Pressure
|
3000 psi
|
Yes- thinking required
|
Yes
|
No
|
|
Tip Size
|
13-17 thou
|
|||
|
Fan angle
|
50⁰
|
Spray For
conventional spray up to 10% Corroless Thinners No 2 should be added
Brush Apply
unthinned, lay on, do not over brush
Mixing Stir
thoroughly before use
Application Temperature 2⁰C to 35⁰C
Ambient Conditions Only apply in conditions
of good ventilation, which should be maintained
during drying. Do not apply when rain, sleet or snow are imminent.
During application and drying time the Relative Humidity should
not exceed 85% and the steel temperature should remain at least
3⁰C
above the dew point.
Stripe coat Stripe coat all sharp edges,
bolts, rivets, welds etc
Flash Point 32⁰C to 55⁰C
Health and safety At all times observe
precautionary notices on containers.